72Ni - 15.5Cr - 0.95Cb - 2.5Ti - 0.70Al - 7.0Fe, Equalized, Precipitation Hardenable
BackThis specification covers a corrosion and heat-resistant nickel alloy in the form of bars, forgings,
flash welded rings, and stock for forging, flash welded rings, or heading.
| Property | Min Value | Max Value |
| N/mmsq 0.2% Yield Strength | 724 | 0 |
| N/mmsq Ultimate Tensile Strength | 1138 | 0 |
| % Elongation | 20 | 0 |
| % Reduction of Area | 25 | 0 |
| Hardness Rockwell B (HRB) | 0 | 0 |
| Hardness Rockwell C (HRC) | 0 | 0 |
| Hardness Brinell (BHN) | 302 | 363 |
| Hardness Vickers (HV) | 0 | 0 |
| % Carbon (C) | 0 | 0.08 |
| % Chromium (Cr) | 14.00 | 17.00 |
| % Manganese (Mn) | 0 | 1.00 |
| % Molybdenum (Mo) | 0 | 0 |
| % Nickel (Ni) | 70 | 0 |
| % Phosphorus (P) | 0 | 0 |
| % Sulphur (S) | 0 | 0.01 |
| % Silicon (Si) | 0 | 0.50 |
| % Iron (Fe) | 5.00 | 9.00 |
| % Copper | 0 | 0.50 |
| % Magnesium | 0 | 0 |
| % Zinc | 0 | 0 |
| % Titanium | 2.25 | 2.75 |
| % Aluminium | 0.40 | 1.00 |
| % Cobalt (Co) | 0 | 1.00 |
| % Zirconium (Zr) | 0 | 0 |
| % Boron (B) | 0 | 0 |
| % Lead (Pb) | 0 | 0 |
| % Bismuth (Bi) | 0 | 0 |
| % Selenium (Se) | 0 | 0 |