Aerocom Tech Centre
Consumable Electrode or Vacuum Induction Melted 1775 °F (968 °C) Solution Heat Treated, Precipitation-Hardenable
BackThis specification covers a corrosion and heat-resistant nickel alloy in the form of bars, forgings,
flash welded rings, and stock for forging, flash welded rings, or heading.
| Property | Min Value | Max Value |
| N/mmsq 0.2% Yield Strength | 1034 | 0 |
| N/mmsq Ultimate Tensile Strength | 1276 | 0 |
| % Elongation | 12 | 0 |
| % Reduction of Area | 15 | 0 |
| Hardness Rockwell B (HRB) | 331 | 0 |
| Hardness Rockwell C (HRC) | 0 | 0 |
| Hardness Brinell (BHN) | 0 | 0 |
| Hardness Vickers (HV) | 0 | 0 |
| % Carbon (C) | 0 | 0.08 |
| % Chromium (Cr) | 17.00 | 21.00 |
| % Manganese (Mn) | 0 | 0.35 |
| % Molybdenum (Mo) | 2.80 | 3.30 |
| % Nickel (Ni) | 50.00 | 55.00 |
| % Phosphorus (P) | 0 | 0.015 |
| % Sulphur (S) | 0 | 0.015 |
| % Silicon (Si) | 0 | 0.35 |
| % Iron (Fe) | 11.0832 | 24.6 |
| % Copper | 0 | 0 |
| % Magnesium | 0 | 0 |
| % Zinc | 0 | 0 |
| % Titanium | 0.65 | 1.15 |
| % Aluminium | 0.20 | 0.80 |
| % Cobalt (Co) | 0 | 1.00 |
| % Zirconium (Zr) | 0 | 0 |
| % Boron (B) | 0 | 0.006 |
| % Lead (Pb) | 0 | 0.0005 |
| % Bismuth (Bi) | 0 | 0.00003 |
| % Selenium (Se) | 0 | 0.0003 |