Aerocom Tech Centre
for use in the softened condition: 460/600 MPa
BackNOTE Sheet and strip of the same composition for use in the hardened and tempered condition are covered by the latest edition
of BS S 514.
This British Standard shall be used in conjunction with the relevant sections of the latest edition
of BS S 500.
| Property | Min Value | Max Value |
| N/mmsq 0.2% Yield Strength | 0 | 0 |
| N/mmsq Ultimate Tensile Strength | 460 | 600 |
| % Elongation | 14 | 0 |
| % Reduction of Area | 0 | 0 |
| Hardness Rockwell B (HRB) | 0 | 0 |
| Hardness Rockwell C (HRC) | 0 | 0 |
| Hardness Brinell (BHN) | 0 | 0 |
| Hardness Vickers (HV) | 0 | 0 |
| % Carbon (C) | 0.17 | 0.25 |
| % Chromium (Cr) | 0 | 0.25 |
| % Manganese (Mn) | 1.3 | 1.7 |
| % Molybdenum (Mo) | 0 | 0.10 |
| % Nickel (Ni) | 0 | 0.40 |
| % Phosphorus (P) | 0 | 0.040 |
| % Sulphur (S) | 0 | 0.040 |
| % Silicon (Si) | 0.10 | 0.35 |
| % Iron (Fe) | 96.87 | 98.43 |
| % Copper | 0 | 0 |
| % Magnesium | 0 | 0 |
| % Zinc | 0 | 0 |
| % Titanium | 0 | 0 |
| % Aluminium | 0 | 0 |
| % Cobalt (Co) | 0 | 0 |
| % Zirconium (Zr) | 0 | 0 |
| % Boron (B) | 0 | 0 |
| % Lead (Pb) | 0 | 0 |
| % Bismuth (Bi) | 0 | 0 |
| % Selenium (Se) | 0 | 0 |