47.5Ni - 22Cr - 1.5Co - 9.0Mo - 0.60W - 18.5Fe, Solution Heat Treated
BackThis specification covers a corrosion and heat-resistant nickel alloy in the form of bars, forgings,
flash welded rings, and stock for forging, flash welded rings, or heading.
| Property | Min Value | Max Value |
| N/mmsq 0.2% Yield Strength | 0 | 0 |
| N/mmsq Ultimate Tensile Strength | 0 | 0 |
| % Elongation | 0 | 0 |
| % Reduction of Area | 0 | 0 |
| Hardness Rockwell B (HRB) | 0 | 0 |
| Hardness Rockwell C (HRC) | 0 | 0 |
| Hardness Brinell (BHN) | 0 | 241 |
| Hardness Vickers (HV) | 0 | 0 |
| % Carbon (C) | 0.05 | 0.15 |
| % Chromium (Cr) | 20.50 | 23.00 |
| % Manganese (Mn) | 0 | 1.00 |
| % Molybdenum (Mo) | 8.00 | 10.00 |
| % Nickel (Ni) | 40.12 | 53.75 |
| % Phosphorus (P) | 0 | 0.040 |
| % Sulphur (S) | 0 | 0.030 |
| % Silicon (Si) | 0 | 1.00 |
| % Iron (Fe) | 17.00 | 20.00 |
| % Copper | 0 | 0.50 |
| % Magnesium | 0 | 0 |
| % Zinc | 0 | 0 |
| % Titanium | 0 | 0.15 |
| % Aluminium | 0 | 0.50 |
| % Cobalt (Co) | 0.50 | 2.50 |
| % Zirconium (Zr) | 0 | 0 |
| % Boron (B) | 0 | 0.010 |
| % Lead (Pb) | 0 | 0 |
| % Bismuth (Bi) | 0 | 0 |
| % Selenium (Se) | 0 | 0 |